Debonding of polymer-metal interfaces often involves both interfacial and cohesive failure. Since the cohesive strength of polymers is usually much greater than the polymer-metal interfacial strength, cohesive failure near the interface is usually desired for enhancing the interfacial adhesion. Roughened surfaces generally produce more cohesive failure; therefore, they are used commonly in practice to obtain better adhesion. This paper develops a fracture mechanics model that can be used to quantitatively predict the amount of cohesive failure once the surface roughness data are given. An epoxy/Al interface was investigated using this fracture mechanics model. The predicted amount of cohesive failure as a function of surface roughness compares very well with the experimentally measured values. It is believed that this model can be extended to other polymer–metal interfaces. Contributed by the Electronic and Photonic Packaging Division for publication in the JOURNAL OF ELECTRONIC PACKAGING. Manuscript received by the EPPD.
Skip Nav Destination
e-mail: jianmin.qu@me.gatech.edu
Article navigation
June 2002
Papers On Reliability
Interfacial Versus Cohesive Failure on Polymer-Metal Interfaces in Electronic Packaging—Effects of Interface Roughness
Qizhou Yao,
Qizhou Yao
The George W. Woodruff School of Mechanical Engineering, Georgia Institute of Technology, Atlanta, GA 30332-0405
Search for other works by this author on:
Jianmin Qu
e-mail: jianmin.qu@me.gatech.edu
Jianmin Qu
The George W. Woodruff School of Mechanical Engineering, Georgia Institute of Technology, Atlanta, GA 30332-0405
Search for other works by this author on:
Qizhou Yao
The George W. Woodruff School of Mechanical Engineering, Georgia Institute of Technology, Atlanta, GA 30332-0405
Jianmin Qu
The George W. Woodruff School of Mechanical Engineering, Georgia Institute of Technology, Atlanta, GA 30332-0405
e-mail: jianmin.qu@me.gatech.edu
Contributed by the Electronic and Photonic Packaging Division for publication in the JOURNAL OF ELECTRONIC PACKAGING. April 16, 2001. Associate Editor: A. Rafanelli.
J. Electron. Packag. Jun 2002, 124(2): 127-134 (8 pages)
Published Online: May 2, 2002
Article history
Received:
April 16, 2001
Online:
May 2, 2002
Citation
Yao , Q., and Qu, J. (May 2, 2002). "Interfacial Versus Cohesive Failure on Polymer-Metal Interfaces in Electronic Packaging—Effects of Interface Roughness ." ASME. J. Electron. Packag. June 2002; 124(2): 127–134. https://doi.org/10.1115/1.1459470
Download citation file:
Get Email Alerts
Impact of Encapsulated Phase Change Material Additives for Improved Thermal Performance of Silicone Gel Insulation
J. Electron. Packag (December 2024)
Special Issue on InterPACK2023
J. Electron. Packag
Related Articles
Special Issue on Poly’2000, London
J. Electron. Packag (December,2002)
Mechanical Reliability and Bump Degradation of ACF Flip Chip Packages Using BCB (Cyclotene™) Bumping Dielectrics Under Temperature Cycling
J. Electron. Packag (June,2004)
Adhesion and Reliability of Epoxy/Glass Interfaces
J. Electron. Packag (December,2001)
On the Mechanical Reliability of Photo-BCB-Based Thin Film Dielectric Polymer for Electronic Packaging Applications
J. Electron. Packag (March,2000)
Related Proceedings Papers
Related Chapters
Applications of Elastic-Plastic Fracture Mechanics in Section XI, ASME Code Evaluations
Online Companion Guide to the ASME Boiler & Pressure Vessel Codes
Introduction and Definitions
Handbook on Stiffness & Damping in Mechanical Design
On the Evaluation of Thermal and Mechanical Factors in Low-Speed Sliding
Tribology of Mechanical Systems: A Guide to Present and Future Technologies