Experimental weld filler metals having high resistance to radiation embrittlement at ≃550 F (288 C) have been developed for quenched and tempered A543 and A542 steel. The filler metals are from a special 2-1/4 Cr-1 Mo-0.40Si-0.10C composition series formulated to study the effects of variable copper, nickel, and manganese contents on weld performance. This report presents an advanced evaluation of weld deposit performance based on new Charpy-V (Cv) and tension data and an analysis of temper embrittlement and radiation embrittlement processes. High fluence assessments confirm the high resistance to radiation embrittlement of the low copper content filler metal group. A 530 F (277 C) irradiation of one typical submerged arc weld deposit to a fluence of 3.8 × 1020 n/cm2 > 1 MeV did not elevate its Cv 30 ft-lb transition temperature to above 275 F (135 C) or reduce its Cv shelf energy level to below 50 ft-lb. Radiation embrittlement saturation was not evident. Temper embrittlement and radiation embrittlement development and the probable mechanisms of copper and phosphorus influences on radiation embrittlement sensitivity are analyzed with the aid of experimental data for the weld metals and A543 plate. Temper embrittlement and radiation embrittlement are shown to be additive effects which can occur simultaneously or sequentially. A separate component of irradiation effects, manifested as a strength increase without embrittlement, is revealed. The enhancement of radiation sensitivity by high copper content (≧0.16–0.27 percent Cu) is related to a copper influence on the radiation elevation of yield strength; the enhancement of radiation sensitivity of phosphorus is ascribed to a detrimental effect similar to that of temper embrittlement. It is proposed that copper acts to pin radiation-induced defect aggregates and dislocation arrays in the matrix and that phosphorus segregates during irradiation to weaken the interface of ferrite platelets and carbides.
Skip Nav Destination
Article navigation
August 1972
This article was originally published in
Journal of Engineering for Industry
Research Papers
Radiation and Temper Embrittlement Processes in Advanced Reactor Weld Metals
J. R. Hawthorne,
J. R. Hawthorne
Naval Research Laboratory, Metallurgy Division, Washington, D. C.
Search for other works by this author on:
E. Fortner
E. Fortner
Babcock & Wilcox Co., Research and Development Division, Alliance, Ohio
Search for other works by this author on:
J. R. Hawthorne
Naval Research Laboratory, Metallurgy Division, Washington, D. C.
E. Fortner
Babcock & Wilcox Co., Research and Development Division, Alliance, Ohio
J. Eng. Ind. Aug 1972, 94(3): 807-814
Published Online: August 1, 1972
Article history
Received:
July 28, 1971
Online:
July 15, 2010
Citation
Hawthorne, J. R., and Fortner, E. (August 1, 1972). "Radiation and Temper Embrittlement Processes in Advanced Reactor Weld Metals." ASME. J. Eng. Ind. August 1972; 94(3): 807–814. https://doi.org/10.1115/1.3428255
Download citation file:
Get Email Alerts
Cited By
Special Section: Manufacturing Science Engineering Conference 2024
J. Manuf. Sci. Eng (November 2024)
Anisotropy in Chip Formation in Orthogonal Cutting of Rolled Ti-6Al-4V
J. Manuf. Sci. Eng (January 2025)
Modeling and Experimental Investigation of Surface Generation in Diamond Micro-Chiseling
J. Manuf. Sci. Eng (February 2025)
Estimation of Temperature Rise in Magnetorheological Fluid-Based Finishing of Thin Substrate: A Theoretical and Experimental Study
J. Manuf. Sci. Eng (February 2025)
Related Articles
Characteristics of the New Embrittlement Correlation Method for the Japanese Reactor Pressure Vessel Steels
J. Eng. Gas Turbines Power (October,2010)
Alternative Method of RT NDT Determination
for Some Reactor Vessel Weld Metals Validated by Fracture Toughness
Data
J. Pressure Vessel Technol (November,1995)
Further Observations on A533-B Steel Plate Tailored for Improved Radiation Embrittlement Resistance
J. Pressure Vessel Technol (May,1976)
Modeling of Irradiation Embrittlement of Reactor Pressure Vessel Steels
J. Eng. Mater. Technol (January,2000)
Related Chapters
Hydrogen Uptake and Embrittlement Susceptibility of Ferrite-Pearlite Pipeline Steels
International Hydrogen Conference (IHC 2016): Materials Performance in Hydrogen Environments
Effect of Hydrogen on Corrosion of Zircaloy-4 under Irradiation
Zirconium in the Nuclear Industry: 20th International Symposium
Part 2, Section II—Materials and Specifications
Companion Guide to the ASME Boiler & Pressure Vessel Code, Volume 1, Second Edition